Mobilgrease 28 (PAIL)

SKU# XOM112687

Be the first to review this product


Quick Overview

Mobilgrease 28 is a supreme performance, wide-temperature, antiwear grease designed to combine the unique features of a polyalphaolefin (PAO) synthetic base fluid with an organo-clay (non-soap) thickener. Its consistency is between an NLGI No. 1 and No. 2 grease. It offers outstanding performance over a wide temperature range. The wax-free nature of the synthetic base fluid, together with its high viscosity index compared to mineral oils, provide excellent low temperature pumpability, very low starting and running torque, and can help reduce operating temperatures in the load zone of rolling element bearings.

The clay thickener gives Mobilgrease 28 a high dropping point value of around 300ºC, which provides excellent stability at high temperatures. Mobilgrease 28 resists water washing, provides superior load-carrying ability, reduces frictional drag, and prevents excessive wear. Tests show that Mobilgrease 28 lubricates effectively rolling element bearings under conditions of high speeds and temperatures. Mobilgrease 28 has also shown excellent ability to lubricate heavily loaded sliding mechanisms, such as wing flap screw jacks.

For more than 30 years, Mobilgrease 28 has been the multi-purpose grease of choice for military and related aviation applications, worldwide.

Product Data Sheet

Mobilgrease 28

Click on image to zoom

More Views

  • Mobilgrease 28

A particular requirement of aviation greases is the need to resist high temperature stresses, while providing excellent starting and low torque at low-temperature. To meet this combination of needs ExxonMobil product formulation scientists chose proprietary synthetic base oils for Mobilgrease 28 because of their low volatility, exceptional thermal/oxidative resistance, and superb low-temperature capability. Formulators chose specific thickener chemistry and a proprietary additive combination which helps maximize the benefits of the synthetic base oils.

Mobilgrease 28 meets the requirements of key military and commercial aviation specifications and has built up a superb reputation for performance and reliability among users around the world.

Mobilgrease 28 provides the following advantages and potential benefits:


Advantages and Potential Benefits

High viscosity index (VI) synthetic base stock with no wax content

Allows wide operating temperature range - outstanding high and low temperature performance.
Provides thicker fluid films protecting against wear of equipment parts operating at high temperature.
Causes low resistance during start-up at very low temperatures

Excellent protection against wear and corrosion

Superb bearing protection and helps extend bearing life and reduce bearing replacement costs

Extreme-pressure protection characteristics

Avoids excessive wear, even under shock load

High thermal/oxidative stability

Long relubrication intervals

High resistance to water washout

Maintains excellent grease performance in adverse weather and other water-exposure conditions


Mobilgrease 28 is designed for the lubrication of plain and rolling bearings at low to high speeds, and splines, screws, worm gears, and other mechanisms where high friction reduction, low wear, and low lubricant friction losses are required. The recommended operating temperature range is -54ºC to 177ºC (-65ºF to 350ºF) with appropriate relubrication intervals.

Mobilgrease 28 is recommended for use in landing wheel assemblies, control systems and actuators, screw jacks, servo devices, sealed-bearing motors, oscillating bearings, and helicopter rotor bearings on military and civil aircraft. Subject to equipment manufacturer approvals, it can also be used on naval shipboard auxiliary machinery and where superseded specifications MIL-G-81322 (WP), MIL-G-7711A, MIL-G-3545B, and MIL-G-25760A are recommended.

Mobilgrease 28 is also recommended for industrial lubrication, including sealed or repackable ball and roller bearings wherever extreme temperature conditions, high speeds, or water washing resistance are factors. Typical industrial applications include conveyor bearings, small alternator bearings operating at temperatures near 177ºC (350ºF), high-speed miniature ball bearings, and bearing applications where oscillatory motion, and vibration create problems.

Mobilgrease 28 is qualified by the U.S. Military under Specification MIL-PRF-81322, General-Purpose, Aircraft, and Specification DOD-G-24508A (Navy) for shipboard auxiliary machinery. It is a U.S. Military Symbol WTR and NATO Code Number G-395 grease.


Mobilgrease 28

Is Approved Against

Quality Level




DOD-G-24508A, Amendment 4



NATO G-395


Typical Properties

Test Methods

Mobilgrease 28 Typicals (1)

MIL-PRF-81322 Limits

NLGI Grade


1 1/2


Thickener Type


Clay (non-soap)




Dark Red




Smooth, buttery


Dropping Point, ºC (ºF)

ASTM D 2265

308 (586)

232 (450) min

Viscosity of Base Oil, cSt

ASTM D 445


at 40ºC




at 100ºC




Low Temp. Torque at -54ºC (-65ºF), Nm (g-cm)

ASTM D 1478





0.98 (10,000) max

Running, after 1 Hr


0.05 (510)

0.098 (1,000) max

Penetration @ 25ºC (77ºF), 60 Stoke Worked, mm/10

ASTM D 217



Extended Worked Penetration Stability, 100,000 Strokes, mm/10

FTM 313


350 max

Oil Separation, 30 Hrs at 177ºC, wt %

ASTM D 6184


2.0 - 8.0

Evaporation Loss, 22 Hrs at 177ºC, wt %

ASTM D 2595


10 max

Copper Strip Corrosion, 24 Hrs at 100ºC

ASTM D 4048


1b max

Four-Ball Wear, Scar dia, mm

ASTM D 2266


0.8 max

Load Wear Index, kgf

ASTM D 2596


30 min

Rust Protection, 48 Hrs at 125ºF, › 1mm dia Corrosion Spots

ASTM D 1743



Water Washout, 1 Hr at 41ºC, wt %

ASTM D 1264


20 max

High Temperature Performance, Hrs at 177ºC

ASTM D 3336


400 min

Oxidation Stability, pressure drop in kPa

ASTM D 942


100 Hrs at 99ºC



83 max

500 Hrs at 99ºC



172 max

Storage Stability, 6 months at 38ºC

FTM 3467



Dirt Count, Particles/mL

FTM 3005


25-74 Micron



1000 max

75 Micron or Larger




Oscillation Friction and Wear, Scar Dia, 35,000 cycles, 90º Angle, Aluminum Bronze Block, mm

Modified ASTM D 3704


6.35 max

Rubber Swell, L Type Synthetic, 1 week at 70ºC (158ºF), vol %

FTM 3603


10 max